O uaea ma uaea, o ē e avea ma ave autū mo le fesiitaiga o le eletise ma fesootaʻiga o faʻamatalaga, e iai le faʻatinoga e faʻalagolago tonu lava i faiga o le faʻamafanafana ma le ufiufi o le uaea. Faatasi ai ma le eseese o manaʻoga faʻaonaponei mo le faʻatinoga o uaea, e fa faiga autū—o le extrusion, longitudinal wrapping, helical wrapping, ma le dip coating—e faʻaalia ai ni tulaga lelei tulaga ese i tulaga eseese. O lenei tusiga e suʻesuʻeina ai le filifilia o meafaitino, le tafe o faiga, ma faʻataʻitaʻiga o faʻaoga o faiga taʻitasi, ma maua ai se faʻavae faʻavae mo le mamanuina ma le filifilia o uaea.
1 Faiga o le Extrusion
1.1 Faiga o Meafaitino
O le faagasologa o le extrusion e faʻaaogaina muamua lava mea faʻapolymer thermoplastic poʻo thermosetting:
① Polyvinyl Chloride (PVC): Tau maualalo, faigofie ona fa'agaoioia, talafeagai mo uaea masani e maualalo le voltage (e pei o uaea masani UL 1061), ae e le lelei le tete'e atu i le vevela (vevela e ≤70°C pe a fa'aaogaina mo se taimi umi).
②Polyethylene ua so'ota'i fa'atasi (XLPE)E ala i le peroxide po'o le fa'avevela o le radiation, e si'itia ai le fua faatatau o le vevela i le 90°C (tulaga fa'atonuina o le IEC 60502), e fa'aaoga mo uaea eletise e feololo ma maualuga le voltage.
③ Thermoplastic Polyurethane (TPU): O le tete'e atu i le olo e ogatasi ma le ISO 4649 Standard Grade A, e fa'aaogaina mo uaea filifili toso a robot.
④ Fluoroplastics (e pei o le FEP): Tete'e atu i le vevela maualuga (200°C) ma le tete'e atu i le 'ele o vaila'au, e ausia ai mana'oga o le uaea va'alele MIL-W-22759.
1.2 Uiga o le Faagasologa
Fa'aaogā se screw extruder e maua ai se ufiufi faifai pea:
① Puleaina o le Vevela: E manaʻomia e le XLPE le pulea o le vevela e tolu vaega (sone fafaga 120°C → sone faʻapipiʻi 150°C → sone faʻafefiloi 180°C).
② Puleaina o le Mafiafi: E tatau ona ≤5% le tulaga ese (e pei ona faamaoti mai i le GB/T 2951.11).
③ Metotia Fa'amālūlū: Fa'amālūlūina fa'asolosolo i totonu o se tane vai e puipuia ai le māvaevae o le tioata.
1.3 Tulaga o Talosaga
① Felauaiga o le Malosiaga: 35 kV ma lalo ifo uaea XLPE ua fa'avevela (GB/T 12706).
② Uaea o Ta'avale: Mea fa'amafanafana PVC e manifinifi ona puipui (ISO 6722 tulaga masani 0.13 mm le mafiafia).
③ Uaea Faapitoa: Uaea coaxial ua fa'a'ofuofuina e le PTFE (ASTM D3307).
2 Faiga o le Afifiina Fa'aumiumi
2.1 Filifiliga o Meafaitino
① Fa'alava U'amea: 0.15 mmlipine u'amea fa'alanu(mana'oga GB/T 2952), lipine alumini ufi palasitika (fausaga Al/PET/Al).
② Mea e taofia ai le vai: Lipine e taofia ai le vai ua ufiufi i le kelu vevela (fua faatatau o le fulafula ≥500%).
③ Meafaitino e Fa'apipi'i ai: Uaea fa'apipi'i alumini ER5356 mo le fa'apipi'iina o le argon arc (tulaga fa'atonuina o le AWS A5.10).
2.2 Tekonolosi Autū
O le faagasologa o le afifiina umi e aofia ai laasaga autu e tolu:
① Fausiaina o fasipepa: Pi'o fasipepa mafolafola i le foliga-U → foliga-O e ala i le fa'ata'avaleina o fasipepa e tele vaega.
② Fa'aauau pea o le fa'avevela: Fa'avevela fa'aoso maualuga (fa'atelega 400 kHz, saoasaoa 20 m/min).
③ Su'esu'ega i luga ole Initaneti: Su'ega o le aloiafi (su'ega o le voltage 9 kV/mm).
2.3 Fa'aoga Masani
① Uaea i lalo o le sami: Afifi uumi uamea vaega lua (malosi fa'amekanika masani a le IEC 60840 ≥400 N/mm²).
② Uaea eliina: Ufiufi alumini e fa'a'ofuofu (MT 818.14 malosi fa'apipi'i ≥20 MPa).
③ Uaea Fesootaiga: Talita afifi uumi e fai i le alumini-palasitika (leiloa o le fesiitaiga ≤0.1 dB/m @1GHz).
3 Faiga o le afifiina o le Helical
3.1 Tuufaatasiga o Meafaitino
① Lipine Mika: O le aofaʻi o Muscovite ≥95% (GB/T 5019.6), vevela e teteʻe atu i le afi 1000°C/90 minute.
② Lipine Semiconducting: O le aofaʻi o le kaponi uliuli e 30%～40% (teteʻe o le voluma 10²～10³ Ω·cm).
③ Lipine Fa'apipi'i: Ata Polyester + ie e le'i lalagaina (mafiafia 0.05 mm ±0.005 mm).
3.2 Fa'asologa o le Fa'agasologa
① Tulimanu e Afifi ai: 25°～55° (o le tulimanu laʻititi e sili atu ona teteʻe i le piʻo).
② Fua Fa'atatau o le Fe'avea'i: 50%～70% (e mana'omia e uaea e tete'e atu i le afi le 100% o le fe'avea'i).
③ Pulea o le Fete'ena'iga: 0.5～2 N/mm² (pulea o le afi servo e tapuni i le matasele).
3.3 Fa'aoga Fou
① Uaea Malosiaga Faaniukilia: Afifiina o le lipine mika e tolu vaega (agavaa le suega LOCA masani a le IEEE 383).
② Uaea Superconducting: Afifiina o le lipine e poloka ai le vai e le semiconducting (fua faatatau taua o le taofia o le tafe eletise ≥98%).
③ Uaea fa'avevela maualuga: PTFE film wrapping (dielectric constant 2.1 @1MHz).
4 Fa'agasologa o le Ufiufi
4.1 Faiga Ufiufi
① Ufiufi Asefala: Fa'aoso 60～80 (0.1 mm) @25°C (GB/T 4507).
② Polyurethane: Faiga e lua-vaega (NCO∶OH = 1.1∶1), pipii ≥3B (ASTM D3359).
③ Nano-ufi: SiO₂ epoxy resin ua suia (su'ega fa'asusu masima >1000 h).
4.2 Fa'aleleia atili o Faiga
① Fa'asusuina i le Vacuum: O le mamafa e 0.08 MPa e tausia mo le 30 minute (fuainumera o le fa'atumuina o pu >95%).
② Fa'amago UV: Umi o le galu 365 nm, malosi 800 mJ/cm².
③ Fa'amagoina i le Fa'asoloatoa: 40°C × 2 itula → 80°C × 4 itula → 120°C × 1 itula.
4.3 Talosaga Faapitoa
① Alavai i Luga: Ufiufi e tete'e atu ai i le 'ele ua suia e le Graphene (ua fa'aitiitia le mafiafia o le masima e 70%).
② Uaea o le Va'a: Ufiufi polyurea e fa'amālōlōina e ia lava (taimi e fa'amālōlō ai māvaevae <24 itula).
③ Uaea ua Tanu: Ufiufi semiconducting (tetee i le eleele ≤5 Ω·km).
5 Faaiuga
Faatasi ai ma le atina'eina o meafaitino fou ma meafaigaluega atamai, o lo'o fa'agasolo pea faiga o ufiufi agai i le fa'apipi'iina ma le fa'atekinolosi. Mo se fa'ata'ita'iga, o le tekinolosi tu'ufa'atasi o le extrusion-longitudinal wrapping e mafai ai ona tu'ufa'atasia le gaosiga o le three-layer co-extrusion + alumini sheath, ma uaea feso'ota'iga 5G e fa'aogaina ai le nano-coating + wrapping composite insulation. O le fa'afouga o faiga i le lumana'i e mana'omia ona maua le paleni lelei i le va o le puleaina o tau ma le fa'aleleia atili o le fa'atinoga, ma fa'amalosia ai le atina'eina maualuga o le tulaga lelei o le alamanuia o uaea.